HANMAC are involved in manufacturing, supplying and exporting a wide range of A420 WPL6 Low Temperature Pipe Fittings.
We are offering an extensive range of ASTM A420 WPL6 Alloy Reducer, which is available in two different forms,
one is Concentric Reducer, and another is Eccentric Reducer types, ie
ASTM A420 WPL6 Concentric Reducers and ASTM A420 WPL6 Eccentric Reducers.
Pipe Reducer are developed using quality steel and other alloys and find usage in sugar mills & distilleries,
pumps & petrochemicals cement & construction industries and steel plants
HANMAC also provide Alloy Fitting, such as Alloy Steel Elbow, Alloy Cap,Alloy Tee
| MODEL | 1. Elbow(90DEG,45DEG,180DEG,30DEG,60DEG) LR and SR |
| 2. Tee(Straight or Equal and Reducing) |
| 3. Reducer(Concentric and Eccentric) |
| 4. Cap |
| Size | Seamless (SMLS) fittings: 1/2"-24", DN15-DN600. |
| Welded fittings (seam) 26"-100", DN650-DN2500. |
| We also accept customized type |
| Thickness | SCH10,SCH20,SCH30, SCH STD, SCH40, SCH60, SCHXS, SCH80, SCH100, SCH120, SCH140, SCH160, SCH XXS. |
| Connection Type | Butt Welded |
| HS CODE | 7307930000 |
| Standard | ASME, ANSI B16.9 |
| JIS B2311/2312/2313 |
| DIN2605 |
| GB12459;GB/T13401 |
| GOST 17375 |
| we can also produce according to drawing and standards provided by customers. |
| Material | ASTM A234 WP11; WP22;WP5;WP9;WP91;WP911; ASTM A420 WPL6 |
| 16Mn; Q345B |
| ST52;ST52.4 |
| Surface | Black or Yellow painting or Customized painting |
| Applications | Petroleum, chemical, machinery, boiler, electric power, shipbuilding, construction, etc |
| Main Market | Turkey, Italy, France, Spain, South Africa, Moroco, Dubai, Iran, Syria, Singapore, Vietnam, Austria, USA, Canada, Mexico, Korea, Thailand, India, Bulgaria, Russia and so on |
| Certificate | ISO9001-2008, |
| Delivery time | 30days after receipt of advanced payment or original LC ,Common size large quantity in stock |
| Payment term | T/T, L/C |
| Inspection | Factory In-House Check or The Third Party Inspection |
| Packaging | Plywood Pallets/ Wooden Case Or As Per customer's request |
| MOQ | No Limit |
| Technics | Hot Forming |
| Origin | China |
| Sample | Sample can be free, but customer have to pay transport cost |
| Chemical Composition (%) of ASTM A420 |
|
| Grade | C | Mn | P | S | Si |
|
| WPL6(1)(2) | 0.3 | 0.60-1.35 | 0.035 | 0.04 | 0.15-0.30 |
|
| Grade | Ni | Cu | Cr | Mo | V | Nb |
| WPL6(1)(2) | 0.4 | 0.4 | 0.3 | 0.12 | 0.08 | 0.02 |
| GENERAL NOTE: |
|
|
|
|
|
|
| All values are maximum unless otherwise indicated. |
| NOTES: |
|
|
|
|
|
|
| (1) For each reduction of 0.01% C below 0.30%, an increase of 0.05% Mn above 1.06% will be permitted, up to a maximum of 1.35%. |
| (2) Fittings made from forgings may have 1.35% max Mn. |
|
|
|
|
|
|
|
| Mechanical properties of ASTM A420 |
|
| Tensile Requirements | WPL6 |
|
|
|
|
|
| Tensile Strength | 60-85 [415-585] |
|
|
|
|
|
| min, ksi [MPa] |
|
|
|
|
| Yield Strength | 35[240] |
|
|
|
|
|
| min, ksi [MPa] |
|
|
|
|
| Where the wall thickness lies between two values above, the min elongation value is determined by the following equations: |
| Longitudinal E=48t+15.00,E=48t+13.00 |
|
|
|
|
|
|
| Transverse E=32t+6.50,E=32t+8.00 |
|
|
|
|
|
|
| E = elongation in 2in [50mm], % |
|
|
|
|
|
|
| t = actual thickness of specimen, in [mm] |
|
|
|
|
|
|